| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 比重 | ASTMD792 | 1.13 | g/cm3 | ||
| 密度 | ISO1183 | 1.13 | g/cm3 | ||
| 收缩率-流动(3.18mm) | 0.90 | % | |||
| 吸水率(24hr) | ASTMD570 | 1.6 | % | ||
| 吸水率(23°C,24hr) | ISO62 | 1.6 | % | ||
| 吸水率(饱和) | ASTMD570 | 9.3 | % | ||
| 吸水率(饱和,23°C) | ISO62 | 9.3 | % | ||
| WaterAbsorption(Equilibrium,50%RH) | ASTMD570 | 2.6 | % | ||
| 吸水率(平衡,23°C,50%RH) | ISO62 | 2.6 | % | ||
| 拉伸模量(23°C) | ISO527-2 | 3500 | MPa | ||
| 抗张强度 | 屈服,-40°C | ASTMD638 | 137 | MPa | |
| 抗张强度 | 屈服,23°C | ASTMD638 | 90.0 | MPa | |
| 抗张强度 | 屈服,80°C | ASTMD638 | 40.0 | MPa | |
| 抗张强度 | Yield,121°C | ASTMD638 | 30.0 | MPa | |
| 拉伸应力(屈服,23°C) | ISO527-2 | 85.0 | MPa | ||
| 抗张强度 | 断裂,-40°C | ASTMD638 | 130 | MPa | |
| 抗张强度 | 断裂,23°C | ASTMD638 | 90.0 | MPa | |
| 抗张强度 | 断裂,80°C | ASTMD638 | 35.0 | MPa | |
| 抗张强度 | Break,121°C | ASTMD638 | 25.0 | MPa | |
| 伸长率 | 屈服,-40°C | ASTMD638 | 3.0 | % | |
| 伸长率 | 屈服,23°C | ASTMD638 | 4.0 | % | |
| 伸长率 | 屈服,80°C | ASTMD638 | 25 | % | |
| 伸长率 | Yield,121°C | ASTMD638 | 27 | % | |
| 拉伸应变(屈服,23°C) | ISO527-2 | 4.0 | % | ||
| 伸长率 | 断裂,-40°C | ASTMD638 | 5.0 | % | |
| 伸长率 | 断裂,23°C | ASTMD638 | 12 | % | |
| 伸长率 | 断裂,80°C | ASTMD638 | >100 | % | |
| 伸长率 | Break,121°C | ASTMD638 | >100 | % | |
| 标称拉伸断裂应变(23°C) | ISO527-2 | 10 | % | ||
| 弯曲模量 | -40°C | ASTMD790 | 3370 | MPa | |
| 弯曲模量 | 23°C | ASTMD790 | 3170 | MPa | |
| 弯曲模量 | 65°C | ASTMD790 | 600 | MPa | |
| 弯曲模量 | 90°C | ASTMD790 | 440 | MPa | |
| 弯曲模量 | 121°C | ASTMD790 | 385 | MPa | |
| 弯曲模量(23°C) | ISO178 | 2800 | MPa | ||
| 弯曲强度 | -40°C | ASTMD790 | 183 | MPa | |
| 弯曲强度 | 23°C | ASTMD790 | 110 | MPa | |
| 弯曲强度 | 65°C | ASTMD790 | 30.0 | MPa | |
| 弯曲强度 | 121°C | ASTMD790 | 21.0 | MPa | |
| 弯曲应力(23°C) | ISO178 | 95.0 | MPa | ||
| 简支梁缺口冲击强度(23°C) | ISO179 | 3.0 | kJ/m2 | ||
| 简支梁无缺口冲击强度(23°C) | ISO179 | NoBreak | |||
| 悬壁梁缺口冲击强度 | -40°C | ASTMD256 | 32 | J/m | |
| 悬壁梁缺口冲击强度 | 23°C | ASTMD256 | 48 | J/m | |
| 洛氏硬度(R级) | ASTMD785 | 120 | |||
| 球压硬度 | ISO2039-1 | 200 | MPa | ||
| 载荷下热变形温度(0.45MPa,未退火) | ASTMD648 | 190 | °C | ||
| 热变形温度(0.45MPa,未退火) | ISO75-2/B | 160 | °C | ||
| 载荷下热变形温度(1.8MPa,未退火) | ASTMD648 | 75.0 | °C | ||
| 热变形温度(1.8MPa,未退火) | ISO75-2/A | 60.0 | °C | ||
| 熔融峰值温度 | ASTMD3418 | 220 | °C | ||
| 溶融温度（DSC） | ISO3146 | 220 | °C | ||
| 线形热膨胀系数-流动 | ASTME831 | 8.1E-5 | cm/cm/°C | ||
| RTIElec | 0.71mm | UL746 | 130 | °C | |
| RTIElec | 1.5mm | UL746 | 130 | °C | |
| RTIElec | 3.0mm | UL746 | 130 | °C | |
| RTIElec | 6.0mm | UL746 | 130 | °C | |
| RTIImp | 0.71mm | UL746 | 95.0 | °C | |
| RTIImp | 1.5mm | UL746 | 105 | °C | |
| RTIImp | 3.0mm | UL746 | 105 | °C | |
| RTIImp | 6.0mm | UL746 | 105 | °C | |
| RTIStr | 0.71mm | UL746 | 95.0 | °C | |
| RTIStr | 1.5mm | UL746 | 105 | °C | |
| 关于德国巴斯夫 Ultramid® 8202C HS BK-102价格 | |||||
| 1.有关“PA6 德国巴斯夫 Ultramid® 8202C HS BK-102”物性表及PA6塑料原料价格以出厂实时数据为准. 2.更多塑料原料的需求请与我们联系，电话同微信：186-2131-7168. | |||||
本文链接：http://www.28at.com/showinfo-41-24732-0.htmlPA6 德国巴斯夫 Ultramid® 8202C HS BK-102
声明：本网页内容旨在传播知识，若有侵权等问题请及时与本网联系，我们将在第一时间删除处理。邮件：2376512515@qq.com
Copyright © 2016-2023 天津谷骐科技有限公司 版权所有 sitemap.xml
违法及侵权请联系：2376512515@qq.com 津ICP备18001702号
津公网安备 12010102000574号