| 其它 其它 注塑 | |
| 特性：玻纤15%强化,一般用途. | |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | ||
| 吸水率 | 23℃，24小时 | ASTM D-570 | 无水｜1.0 | % | |
| 吸水率 | 23℃，24小时 | ASTM D-570 | 1.9%水｜- | % | |
| 比重 | ASTM D-792 | 无水｜1.26 | |||
| 比重 | ASTM D-792 | 1.9%水｜- | |||
| 抗拉屈服强度 | -40℃ | ASTM D-638 | 无水｜1500 | Kg/cm2 | |
| 抗拉屈服强度 | -40℃ | ASTM D-638 | 1.9%水｜- | Kg/cm2 | |
| 挠曲模量 | 80℃ | ASTM D-790 | 无水｜27000 | Kg/cm2 | |
| 挠曲模量 | 80℃ | ASTM D-790 | 1.9%水｜21000 | Kg/cm2 | |
| IZOD冲击强度 | 23℃，V缺口1/2 | ASTM D-256 | 无水｜6 | kgcm/cm | |
| IZOD冲击强度 | 23℃，V缺口1/2 | ASTM D-256 | 1.9%水｜- | kgcm/cm | |
| 洛氏硬度 | 23℃ | ASTM D-785 | 无水｜120 | R-标度 | |
| 洛氏硬度 | 23℃ | ASTM D-785 | 1.9%水｜- | R-标度 | |
| 挠曲模量 | 23℃ | ASTM D-790 | 无水｜53000 | Kg/cm2 | |
| 挠曲模量 | 23℃ | ASTM D-790 | 1.9%水｜34000 | Kg/cm2 | |
| 抗拉屈服强度 | 23℃ | ASTM D-638 | 无水｜1150 | Kg/cm2 | |
| 抗拉屈服强度 | 23℃ | ASTM D-638 | 1.9%水｜850 | Kg/cm2 | |
| 断裂伸长率 | 80℃ | ASTM D-638 | 无水｜+4309:4325 | % | |
| 断裂伸长率 | 80℃ | ASTM D-638 | 1.9%水｜- | % | |
| 挠曲强度 | 23℃ | ASTM D-790 | 无水｜1600 | Kg/cm2 | |
| 挠曲强度 | 23℃ | ASTM D-790 | 1.9%水｜1150 | Kg/cm2 | |
| 洛氏硬度 | 23℃ | ASTM D-785 | 无水｜95 | M-标度 | |
| 洛氏硬度 | 23℃ | ASTM D-785 | 1.9%水｜- | M-标度 | |
| 挠曲模量 | -40℃ | ASTM D-790 | 无水｜63000 | Kg/cm2 | |
| 挠曲模量 | -40℃ | ASTM D-790 | 1.9%水｜60000 | Kg/cm2 | |
| 断裂伸长率 | -40℃ | ASTM D-638 | 无水｜3 | % | |
| 断裂伸长率 | -40℃ | ASTM D-638 | 1.9%水｜- | % | |
| IZOD冲击强度 | 23℃，无缺口1/8 | 无水｜30 | kgcm/cm2 | ||
| IZOD冲击强度 | 23℃，无缺口1/8 | 1.9%水｜- | kgcm/cm2 | ||
| 断裂伸长率 | 23℃ | ASTM D-638 | 无水｜4 | ||
| 断裂伸长率 | 23℃ | ASTM D-638 | 1.9%水｜7 | ||
| 抗拉屈服强度 | 80℃ | ASTM D-638 | 无水｜600 | Kg/cm2 | |
| 抗拉屈服强度 | 80℃ | ASTM D-638 | 1.9%水｜- | Kg/cm2 | |
| 挠曲强度 | 80℃ | ASTM D-790 | 无水｜1050 | Kg/cm2 | |
| 挠曲强度 | 80℃ | ASTM D-790 | 1.9%水｜- | Kg/cm2 | |
| 抗剪强度 | 23℃ | ASTM D-732 | 无水｜800 | Kg/cm2 | |
| 抗剪强度 | 23℃ | ASTM D-732 | 1.9%水｜- | Kg/cm2 | |
| 体积电阻率 | ASTM D-257 | 无水｜1015 | Ω.cm | ||
| 体积电阻率 | ASTM D-257 | 1.9%水｜1012-1013 | Ω.cm | ||
| 介电强度 | 1/8 | ASTM D-149 | 无水｜20 | KV/mm | |
| 介电强度 | 1/8 | ASTM D-149 | 1.9%水｜- | KV/mm | |
| 熔点 | 差示扫描测热计DSC | 无水｜265 | ℃ | ||
| 熔点 | 差示扫描测热计DSC | 1.9%水｜- | ℃ | ||
| 线性热膨胀系数 | ASTM D-696 | 无水｜4 | ×10-5cm/cm/℃ | ||
| 线性热膨胀系数 | ASTM D-696 | 1.9%水｜- | ×10-5cm/cm/℃ | ||
| 热挠曲温度 | 18.6kg/cm2 | ASTM D-648 | 无水｜245 | ℃ | |
| 热挠曲温度 | 18.6kg/cm2 | ASTM D-648 | 1.9%水｜- | ℃ | |
| 比热 | 无水｜0.42 | Cal/g℃ | |||
| 比热 | 1.9%水｜- | Cal/g℃ | |||
| UL-94抗燃级 | 1/16 | UL 94 | 无水｜HB | ||
| UL-94抗燃级 | 1/16 | UL 94 | 1.9%水｜- | ||
| 强化含量 | 无水｜15 | WT% | |||
| 强化含量 | 1.9%水｜- | WT% | |||
| 关于日本东丽 CM3001G-15价格 | |||||
| 1.有关“PA66 日本东丽 CM3001G-15”物性表及PA66塑料颗粒价格以出厂实时数据为准. 2.更多塑料颗粒的需求请与我们联系. | |||||
本文链接：http://www.28at.com/showinfo-42-26336-0.htmlPA66 日本东丽 CM3001G-15
声明：本网页内容旨在传播知识，若有侵权等问题请及时与本网联系，我们将在第一时间删除处理。邮件：2376512515@qq.com
上一篇： PA66 日本东丽 CM3004-V0
下一篇： PA66 日本东丽 CM3001G-30
Copyright © 2016-2023 天津谷骐科技有限公司 版权所有 sitemap.xml
违法及侵权请联系：2376512515@qq.com 津ICP备18001702号
津公网安备 12010102000574号